Movster 12 strands
Combining the abrasion resistance of Polyester with the tenacity of Movline bi-polymer fiber, its round plait construction provides a soft and flexible handling. Lighter than traditional combo ropes and with very low water absorption, this floating line is an economic solution when compared to regular polyester ropes.
-
- High abrasion and wear resistance
- 12-14% lighter than traditional combo ropes
- Very low water absorption
- Flexible and smooth handling, non kinking and non rotating
-
-
- Raw material: Mixed Polyolefin / Polyester
- Specific Gravity: 1,00 (floats)
- Melting Point: 165ºC / 265ºC
- Elongation at % of BS:
25% …. 3,9%
50% …. 8,3%
Diameter Size
Circ.Weight Breaking Load mm Inches Inches Ktex Kg/100m lbs/100ft Kgf lbf kN 24 1 3 279 27,9 18,7 9 820 21 649 96,3 26 1 1/32 3 1/4 328 32,8 22 11 523 25 403 113 28 1 1/8 3 1/2 380 38 25,5 13 256 29 225 130 30 1 1/4 3 3/4 437 43,7 29,4 15 092 33 271 148 32 1 5/16 4 497 49,7 33,4 17 029 37 543 167 36 1 1/2 4 1/2 629 62,9 42,3 21 414 47 209 210 40 1 5/8 5 776 77,6 52,1 26 207 57 775 257 44 1 3/4 5 1/2 939 93,9 63,1 31 407 69 240 308 48 2 6 1 110 111 74,6 37 118 81 829 364 52 2 1/8 6 1/2 1 320 132 88,7 43 236 95 318 424 56 2 1/4 7 1 520 152 102,1 49 864 109 930 489 60 2 1/2 7 1/2 1 750 175 117,6 56 900 125 442 558 64 2 5/8 8 1 990 199 133,7 64 344 141 853 631 68 2 3/4 8 1/2 2 250 225 151,2 72 094 158 938 707
In accordance to ISO 14686-2004
Breaking load values stated shall be reduced by 10 % in the case of a rope with eye-spliced terminations.
- Mooring lines
- Anchor lines
- Tie-up lines
- Barge working lines
-
- Raw material: Mixed Polyolefin / Polyester
- Specific Gravity: 1,00 (floats)
- Melting Point: 165ºC / 265ºC
- Elongation at % of BS:
25% …. 3,9%
50% …. 8,3%
| Diameter | Size Circ. | Weight | Breaking Load | |||||
| mm | Inches | Inches | Ktex | Kg/100m | lbs/100ft | Kgf | lbf | kN |
| 24 | 1 | 3 | 279 | 27,9 | 18,7 | 9 820 | 21 649 | 96,3 |
| 26 | 1 1/32 | 3 1/4 | 328 | 32,8 | 22 | 11 523 | 25 403 | 113 |
| 28 | 1 1/8 | 3 1/2 | 380 | 38 | 25,5 | 13 256 | 29 225 | 130 |
| 30 | 1 1/4 | 3 3/4 | 437 | 43,7 | 29,4 | 15 092 | 33 271 | 148 |
| 32 | 1 5/16 | 4 | 497 | 49,7 | 33,4 | 17 029 | 37 543 | 167 |
| 36 | 1 1/2 | 4 1/2 | 629 | 62,9 | 42,3 | 21 414 | 47 209 | 210 |
| 40 | 1 5/8 | 5 | 776 | 77,6 | 52,1 | 26 207 | 57 775 | 257 |
| 44 | 1 3/4 | 5 1/2 | 939 | 93,9 | 63,1 | 31 407 | 69 240 | 308 |
| 48 | 2 | 6 | 1 110 | 111 | 74,6 | 37 118 | 81 829 | 364 |
| 52 | 2 1/8 | 6 1/2 | 1 320 | 132 | 88,7 | 43 236 | 95 318 | 424 |
| 56 | 2 1/4 | 7 | 1 520 | 152 | 102,1 | 49 864 | 109 930 | 489 |
| 60 | 2 1/2 | 7 1/2 | 1 750 | 175 | 117,6 | 56 900 | 125 442 | 558 |
| 64 | 2 5/8 | 8 | 1 990 | 199 | 133,7 | 64 344 | 141 853 | 631 |
| 68 | 2 3/4 | 8 1/2 | 2 250 | 225 | 151,2 | 72 094 | 158 938 | 707 |
In accordance to ISO 14686-2004
Breaking load values stated shall be reduced by 10 % in the case of a rope with eye-spliced terminations.