Combo 12 strands
This blended rope combines the best properties of Polyester fiber with our Movline Plus bi-polymer fiber, in a unique 12 strands construction where every single Movline yarn is covered with Polyester, giving it an exceptional wearing resistance and strength with significantly less handling weight than regular polyester ropes.
-
- Exceptional abrasion and wear resistance on H-bitts
- 18-20 % lighter than regular polyester ropes
- Less water absorption than an all polyester ropes
- Flexible and smooth, non kinking and non rotating
-
-
- Raw material: Mixed Polyolefin / Polyester
- Specific Gravity: 1,16 (sinks)
- Melting Point: 165ºC / 265ºC
- Elongation at % of BS:
25% …. 3,2%
50% …. 6,7%
Diameter Size
Circ.Weight Breaking Load mm Inches Inches Ktex Kg/100m lbs/100ft Kgf lbf kN 24 1 3 319 31,9 21,4 10 911 24 054 107 26 1 1/32 3 1/4 374 37,4 25,1 12 747 28 101 125 28 1 1/8 3 1/2 434 43,4 29,2 14 684 32 372 144 30 1 1/4 3 3/4 498 49,8 33,5 16 723 36 868 164 32 1 5/16 4 566 56,6 38 18 967 41 814 186 36 1 1/2 4 1/2 717 71,7 48,2 23 759 52 380 233 40 1 5/8 5 885 88,5 59,5 29 062 64 070 285 44 1 3/4 5 1/2 1 070 107 71,9 34 874 76 884 342 48 2 6 1 270 127 85,3 41 197 90 822 404 52 2 1/8 6 1/2 1 500 150 100,8 48 029 105 884 471 56 2 1/4 7 1 730 173 116,2 55 371 122 070 543 60 2 1/2 7 1/2 1 990 199 133,7 63 223 139 380 620 64 2 5/8 8 2 270 227 152,5 71 482 157 589 701 68 2 3/4 8 1/2 2 560 256 172 80 150 176 698 786
In accordance to ISO 14686:2004.
Breaking load values stated shall be reduced by 10% in the case of a rope with eye-spliced terminations.
- Mooring lines
- Anchor lines
- Tug boat H-Bitt working lines
- Barge working lines
-
- Raw material: Mixed Polyolefin / Polyester
- Specific Gravity: 1,16 (sinks)
- Melting Point: 165ºC / 265ºC
- Elongation at % of BS:
25% …. 3,2%
50% …. 6,7%
| Diameter | Size Circ. | Weight | Breaking Load | |||||
| mm | Inches | Inches | Ktex | Kg/100m | lbs/100ft | Kgf | lbf | kN |
| 24 | 1 | 3 | 319 | 31,9 | 21,4 | 10 911 | 24 054 | 107 |
| 26 | 1 1/32 | 3 1/4 | 374 | 37,4 | 25,1 | 12 747 | 28 101 | 125 |
| 28 | 1 1/8 | 3 1/2 | 434 | 43,4 | 29,2 | 14 684 | 32 372 | 144 |
| 30 | 1 1/4 | 3 3/4 | 498 | 49,8 | 33,5 | 16 723 | 36 868 | 164 |
| 32 | 1 5/16 | 4 | 566 | 56,6 | 38 | 18 967 | 41 814 | 186 |
| 36 | 1 1/2 | 4 1/2 | 717 | 71,7 | 48,2 | 23 759 | 52 380 | 233 |
| 40 | 1 5/8 | 5 | 885 | 88,5 | 59,5 | 29 062 | 64 070 | 285 |
| 44 | 1 3/4 | 5 1/2 | 1 070 | 107 | 71,9 | 34 874 | 76 884 | 342 |
| 48 | 2 | 6 | 1 270 | 127 | 85,3 | 41 197 | 90 822 | 404 |
| 52 | 2 1/8 | 6 1/2 | 1 500 | 150 | 100,8 | 48 029 | 105 884 | 471 |
| 56 | 2 1/4 | 7 | 1 730 | 173 | 116,2 | 55 371 | 122 070 | 543 |
| 60 | 2 1/2 | 7 1/2 | 1 990 | 199 | 133,7 | 63 223 | 139 380 | 620 |
| 64 | 2 5/8 | 8 | 2 270 | 227 | 152,5 | 71 482 | 157 589 | 701 |
| 68 | 2 3/4 | 8 1/2 | 2 560 | 256 | 172 | 80 150 | 176 698 | 786 |
In accordance to ISO 14686:2004.
Breaking load values stated shall be reduced by 10% in the case of a rope with eye-spliced terminations.